Market availability of aluminum alloys for laser powder bed fusion (L-PBF) is still highly limited in comparison to conventional manufacturing processes. The demand for high-strength but inexpensive alloys specifically designed for L-PBF is high. This demand has led to research on a variety of adapted conventional alloys which are still limited to utilize the full potential of L-PBF. Scalmalloy® (Al–Mg–Sc–Zr) satisfies the demand for high-strength L-PBF-alloys but needs a high energy input and has troubles with evaporation of Mg. Scancromal® (Al–Cr–Sc–Zr) is a novel alloying system for L-PBF and was first introduced in 2019 with the possibility of higher build rates and comparable strengths to Scalmalloy®. In this paper, a more economic low Sc-containing version of Scancromal® is presented. A parameter study was performed for 100 μm layer thickness reaching high build rates of about 47 cm3 h−1 . Hardness tests for different parameters were carried out and showed a stable process window with a hardness comparable to AlSi10Mg. Additionally, two-dimensional multilayer process simulations showed a potential for increasing the layer thickness to 150 μm and therefore a significant increase in build rate of up to 70 cm3 h−1 highlighting the high productivity potential of Al–Cr alloys for L-PBF.     «

Market availability of aluminum alloys for laser powder bed fusion (L-PBF) is still highly limited in comparison to conventional manufacturing processes. The demand for high-strength but inexpensive alloys specifically designed for L-PBF is high. This demand has led to research on a variety of adapted conventional alloys which are still limited to utilize the full potential of L-PBF. Scalmalloy® (Al–Mg–Sc–Zr) satisfies the demand for high-strength L-PBF-alloys but needs a high energy input an...     »