Slackened carbon stripper foils of 3 to 5 μg/cm2 produced by vacuum evaporation-condensation were graphitized by annealing at about 3300 K with a pulsed laser beam (1.06 μm). An average crystal size of 10 nm was measured by electron diffraction. The texture of the 002-plane is parallel to the surface of the foil as known from slightly annealed carbon foils. Radiation damages caused by high doses of heavy ions dramatically change the crystal structure. Electron diffraction patterns reveal newly formed graphite crystals with their 002-plane perpendicular to the texture. Compared to carbon foils of the same kind, but not graphitized, a lifetime prolongation of a factor of two was achieved for such foils tested in the terminal of the Munich MP tandem. The slope of the curve for heavy-ion transmission through carbon stripper foils varies for foils of the same kind and for different ion-beam conditions. «
Slackened carbon stripper foils of 3 to 5 μg/cm2 produced by vacuum evaporation-condensation were graphitized by annealing at about 3300 K with a pulsed laser beam (1.06 μm). An average crystal size of 10 nm was measured by electron diffraction. The texture of the 002-plane is parallel to the surface of the foil as known from slightly annealed carbon foils. Radiation damages caused by high doses of heavy ions dramatically change the crystal structure. Electron diffraction patterns reveal newly f... »